Zeolite catalyst and method

ABSTRACT

A catalyst is formed from a phosphorus-containing ZSM-5-type zeolite. The ZSM-5-type zeolite has a silica/alumina molar ratio of at least 200. The phosphorus-containing ZSM-5-type zeolite also has a phosphorus content of at least 8% by weight of zeolite and has multiple phosphorus species exhibited by at least two  31 P MAS NMR peaks with maxima at from about 0 to about −50 ppm. The catalyst may be used in aromatic alkylation by contacting the catalyst with a feed of an aromatic hydrocarbon and an alkylating agent under reaction conditions suitable for aromatic alkylation.

This application is a continuation-in-part of U.S. patent application Ser. No. 10/831,729, entitled “Method of Modifying Zeolite Catalyst,” filed Apr. 23, 2004 now U.S. Pat. No. 7,285,511, which is herein incorporated by reference in its entirety.

TECHNICAL FIELD

The invention relates generally to the alkylation of aromatic compounds and catalysts used for such reactions.

BACKGROUND

Para-xylene is a valuable substituted aromatic compound due to its great demand for production of terephthalic acid, a major component in forming polyester fibers and resins. It can be commercially produced from hydrotreating of naphtha (catalytic reforming), steam cracking of naphtha or gas oil, and toluene disproportionation.

Alkylation of toluene with methanol, which is also known as toluene methylation, has been used in laboratory studies to produce para-xylene. Toluene methylation has been known to occur over acidic catalyst, particularly over zeolite or zeolite-type catalyst. In particular, ZSM-5-type zeolite, zeolite Beta and silicaaluminophosphate (SAPO) catalysts have been used for this process. Generally, a thermodynamic equilibrium mixture of ortho (o)-, meta (m)- and para (p)-xylenes can be formed from the methylation of toluene, as is illustrated by the reaction below.

Thermodynamic equilibrium compositions of o-, m-, and p-xylenes may be around 25, 50 and 25 mole %, respectively, at a reaction temperature of about 500° C. Such toluene methylation may occur over a wide range of temperatures, however. Para-xylene can be separated from mixed xylenes by a cycle of adsorption and isomerization. Byproducts such as C9+ and other aromatic products can be produced by secondary alkylation of the xylene product.

A significantly higher amount of p-xylene can be obtained in toluene methylation reaction if the catalyst has shape selective properties. Shape selective properties can be obtained in modified zeolite catalysts by modifying zeolite pore opening size, inactivation of the external surface of the zeolite or controlling zeolite acidity. Toluene methylation may occur over modified ZSM-5 or ZSM-5-type zeolite catalyst giving xylene products containing significantly greater amounts of p-xylene than the thermodynamic concentration.

Phosphoric acid and other phosphorus-containing compounds have been used to modify ZSM-5 zeolite catalysts to provide shape selective properties. U.S. Pat. No. 6,504,072, for instance, discloses the treatment of ZSM-5 zeolite catalyst with phosphorus (P) to control the reduction of diffusivity and pore volume prior to severe steaming to provide a para-selective catalyst. U.S. Pat. No. 4,554,394 discusses the treatment of ZSM-5 zeolites with a vapor phase organophosphorus reagent to provide para-selective properties. Although such phosphorus-treated ZSM-5 catalysts may have a high selectivity for p-xylene, they tend to deactivate at a very fast rate. For example, the catalyst may lose greater than 50% of its initial activity within a day. This may possibly be due to coke deposition on the catalyst.

Because there are a number of technical hurdles for toluene methylation to be commercially successful, improvements are needed.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present invention, reference is now made to the following descriptions taken in conjunction with the accompanying figures, in which:

FIG. 1 is a plot of BET surface area of different H₃PO₄-modified ZSM-5 zeolite catalysts as a function of the amount of phosphorus used in the modifications;

FIG. 2 is a plot of total pore volume of different H₃PO₄-modified ZSM-5 zeolite catalysts as a function of the amount of phosphorus used in the modification;

FIG. 3 shows ²⁷Al MAS-NMR spectra of (a) NH₄-ZSM-5 zeolite having SiO₂/Al₂O₃ mole ratio 280, and of (b) phosphorus-modified ZSM-5 zeolite catalyst;

FIG. 4 shows ³¹P MAS-NMR spectra of phosphorus-modified catalysts after drying/calcining at different temperatures: (a) dried at 60° C. (Catalyst T), (b) dried at 250° C. (Catalyst U), (c) dried at 350° C. (Catalyst V), and (d) calcined at 510° C. (Catalyst W);

FIG. 5 is a plot of wt % total xylenes and selectivity to total xylenes and p-xylene for a liquid product stream obtained from toluene methylation over H₃PO₄ modified ZSM-5 zeolite catalysts having a starting SiO₂/Al₂O₃ mole ratio of 30 as a function of amount of phosphorus used in the modification; and

FIG. 6 is a plot of wt % total xylenes and selectivity to total xylenes and p-xylene for a liquid product stream obtained from toluene methylation over H₃PO₄ modified ZSM-5 zeolite catalysts having a starting SiO₂/Al₂O₃ mole ratio of 280 as a function of amount of phosphorus used in the modification.

DETAILED DESCRIPTION

As used herein, the expression “ZSM-5-type” is meant to refer to those zeolites that are isostructurally the same as ZSM-5 zeolites. Additionally, the expressions “ZSM-5” and “ZSM-5-type” may be used herein interchangeably to encompass one another and should not be construed in any limiting sense. The ZSM-5 zeolite catalysts and their preparation are described in U.S. Pat. No. 3,702,886, which is herein incorporated by reference.

As used herein, catalytic activity can be expressed as the % moles of toluene converted with respect to the moles of toluene fed and can be defined as: Mole % Toluene Conversion=[(T _(i) −T _(o))/T _(i)]×100  (2) where, T_(i) is the number of moles of toluene fed and T_(o) is the number of moles toluene unreacted. As used herein, selectivity for mixed-xylenes may be expressed as: Mole % Mixed Xylene Selectivity=[X _(mx)/(T _(i) −T _(o))]×100  (3) where, X_(mx) is the number of moles of total (o-, m- or p-) xylenes in the product. As used herein, selectivity for p-xylene may be expressed as: Mole % p-Xylene Selectivity=(X _(p) /X _(mx))×100  (4) where, X_(p) is the number of moles of p-xylene.

Modification of ZSM-5 zeolite with phosphorus containing compound(s) and heat treatment may cause the formation of certain phosphorus-species within the zeolite pores and channels, which may result in the reduction of surface area and pore volume. Such modified catalysts may provide increased para-selectivity without the need for subsequent steaming at a high temperature (e.g., 700° C. or higher) or additional treatment of the catalyst. The phosphorus-modified ZSM-5 catalysts provide increased activity and selectivity for aromatic alkylation. In certain instances, increased catalyst activity and total xylenes selectivity may be achieved during use in toluene methylation for particular ZSM-5 zeolite catalysts, while still providing high p-xylene selectivity.

In the present invention, ZSM-5 zeolite is modified with a P-containing compound and heat treated to provide shape selectivity. The starting ZSM-5 zeolite may be an NH₄- or H-form zeolite, which may be in the form of a powder or any other form. In the present invention, the ZSM-5 zeolite catalyst may include those having a silica/alumina molar ratio of greater than 25 prior to modification with a phosphorus containing compound. As is discussed below, the silica/alumina ratio of the initial ZSM-5 zeolite catalyst may have an effect on catalyst activity and xylene selectivity of the subsequently treated catalyst in toluene methylation. In certain instances, the SiO₂/Al₂O₃ mole ratio of starting ZSM-5 may be from 200, 280, 300 to 1000 or more to achieve higher activity with increased p-xylene selectivity.

The phosphorus compound may be a phosphorus-containing acid, such as phosphoric acid (H₃PO₄) and phosphorus acid (H₃PO₃). For phosphorus-containing acids, the acid may be used at a concentration of greater than 50 wt %, with from 50 wt % to about 85 wt % being suitable. The phosphorus compound may also include other non-acid phosphorus-containing compounds, such as ammonium hydrogen phosphate ((NH₄)₂HPO₄). The amount of phosphorus used may provide a phosphorus content of the treated catalyst of from 0.04 g P/g zeolite or more. In certain applications, phosphorus may be incorporated into the catalyst in amounts of from 0.08 g P/g zeolite or more, more specifically from about 0.09 g P/g zeolite to about 0.10 g P/g zeolite or to about 0.15 g P/g zeolite.

The phosphorus treatment may be carried out by various techniques. This may include slurry evaporation and wet incipient methods. In slurry evaporation, the phosphorus may be incorporated into the catalyst by preparing a slurry of the zeolite and an aqueous solution of the phosphorus compound. Heating of the slurry may be used to facilitate treatment of the zeolite catalyst and to evaporate liquids. Heating of the slurry to temperatures of from about 25° C. or more, with from 70° C. to about 100° C. being suitable in most instances. The slurry may also be stirred or agitated during this step to ensure uniform treatment. The evaporation of the liquid from the zeolite slurry can be alternatively achieved by spray-dry technique which is well known in the art.

In the wet incipient method, an aqueous solution of the phosphorus compound is added, such as by spraying, to dry zeolite without forming a slurry. The dry zeolite, which may be initially in the form of a powder, may be mixed with the phosphorus compound to form a dough. If necessary, water may be added to the mixture to facilitate formation of the zeolite dough. The dough may then be heated at similar temperatures to those of the slurry technique to facilitate evaporation of water.

The P-treated zeolite may be calcined at 250° C. or more, more particularly, a temperature between 300° C. and 600° C., more particularly from about 400° C. to about 570° C., in an environment containing oxygen, typically air. Calcining may take place over time, typically from several minutes to one hour or more. Calcining may also take place by gradually increasing the temperature over time

The phosphorus-modified zeolite catalyst may be used unbound or be bound with a binder. Examples of suitable binders include such materials as alumina, clay, and silica. Those techniques used for preparing the bound catalyst are well known in the art.

The treated ZSM-5 zeolite catalyst may provide a total pore volume of from about 0.2 ml/g or less. More particularly, the total pore volume may range from about 0.18 ml/g to about 0.07 ml/g. The BET surface area of the ZSM-5 zeolite catalyst may range from less than 300 m²/g to about 10 m²/g.

The phosphorus-modified catalyst contains an insignificant amount of tetrahedral/structural Al in the zeolite framework showing a weak ²⁷Al-MAS NMR peak at around 50 ppm, but the catalyst may contain “debris” or extra framework aluminum (EFAl) inside zeolite pores showing a strong ²⁷Al-MAS NMR peak at about −14 ppm. The ratio of framework aluminum over extra-framework aluminum for the treated zeolite catalyst may range from about 0.12 to 0.25.

The phosphorus modified zeolite contains different P-species showing ³¹P-MAS NMR peak(s) having maxima at from about 0 ppm to about −50 ppm. The P-species may be free phosphate, or bonded to extra-framework Al, or AlPO/SAPO, or polyphosphate type species.

The treated catalyst may be used as a non-steamed catalyst in toluene methylation. The phosphorus-treated ZSM-5 zeolite catalyst may also be steamed at low or mild temperatures. The steaming may occur by contacting the catalyst with steam in the presence of hydrogen gas or other inert gases. Steaming temperatures may range from about 150° C. to about 250° C., 300° C. or 350° C. This may be accomplished separately or in situ within the reactor, prior to any aromatic alkylation reaction or introduction of any reaction feed. Steaming may be conducted from a few minutes to several hours. The use of catalyst steaming at mild temperatures is described in the co-pending U.S. patent application Ser. No. 11/122,919, filed May 5, 2005, entitled “Hydrothermal Treatment of Phosphorus-Modified Zeolite Catalysts,” which is herein incorporated by reference.

The modified catalyst may be contacted with an appropriate feed of an aromatic hydrocarbon and an alkylating agent under alkylation reaction conditions to carry out aromatic alkylation. The catalyst has particular application for use in toluene methylation utilizing a toluene/methanol feed. A gas cofeed may also be optionally used. The cofeed gas may include hydrogen or an inert gas. The cofeed gas may be used in an amount of at least 0.1 mole per mole of aromatic alkylation feed. As used herein, the expression “alklyation feed” is meant to encompass the aromatic compound and the alkylating agent. As used herein, the expression “methylation feed” is meant to encompass the feed of toluene and methanol.

In addition to cofeed gas, water or steam may also be introduced into the reactor as cofeed along with the alkylation feed. The water or steam used for the methylation reaction may be introduced with or without hydrogen or inert gas as cofeed with the alkylation feed to the reactor during the start up of the alkylation reaction or it may be introduced subsequent to initial start up. In either case, liquid water may be added and vaporized prior to its mixing with cofeed gas (if any) and alkylation feed.

The reactor pressure for toluene methylation or other aromatic alkylation may vary, but typically ranges from about 10 to about 1000 psig. Reactor temperatures may typically range from 400 to 700° C.

The reaction may be carried in a variety of different reactors that are commonly used for carrying out aromatic alkylation reactions. Single or multi reactors in series and/or parallel are suitable for carrying out the toluene methylation.

The modified catalyst is useful in toluene methylation for preparing a xylene product from a feed of toluene and methanol that has increased selectivity for p-xylene. In particular, the catalyst may provide greater than 80%, 85% and 90% para-xylene selectivity when used in toluene methylation. Additionally, in certain instances, greater than 90% of total xylene selectivity may be achieved.

The following examples serve to further illustrate the invention.

EXAMPLES

Catalyst Preparation

Catalyst A-I

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 30. An aqueous slurry containing 11.63 g of NH₄-ZSM-5 zeolite and 50 ml of deionized water was prepared in a 400 ml beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a magnetic stir bar. The temperature of the suspension was maintained around 90° C. 1.08 g of phosphoric acid (85 wt % in aqueous) was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The phosphoric-acid modified zeolite was dried at 90° C. to 120° C. for at least four hours and at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined zeolite was then crushed and sized using 20 and 40 mesh screens. A series of catalysts A-H (see Table 1) were prepared by varying the amount of phosphoric acid with respect to the amount of starting NH₄-ZSM-5 powder. A non-phosphorus ZSM-5 (Catalyst I) was also prepared by calcining (using the same temperature profile described above) the NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 30. BET surface area (SA) and total pore volume (PV) (measured by N₂ adsorption) for Catalysts A-I are shown in Table 1 and in FIGS. 1 and 2.

TABLE 1 Water, Zeolite H₃PO₄ P, g/g PV, Catalyst ml Powder, g Content, g^(a) zeolite^(a) SA, m2/g ml/g A 100  46.50 4.00 0.023 266.4 0.483 B 50 11.63 1.08 0.025 259.0 0.340 C 50 11.63 2.52 0.058 157.8 0.212 D 50 11.64 4.04 0.093 66.9 0.189 E 50 11.63 6.01 0.139 24.0 0.183 F 50 11.63 8.05 0.186 18.6 0.179 G 50 11.64 12.51 0.279 14.2 0.077 H 50 11.64 16.01 0.370 9.7 0.079 I — — 0 0 357.2 0.579 ^(a)Total amount of phosphoric acid (85% in aqueous) or P used in the preparation

As can be seen from Table 1 and FIGS. 1 and 2, a sharp decrease in BET surface area (SA) and total pore volume (PV) of the zeolite Catalysts A-H prepared by using starting NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio of 30 with increasing amounts of phosphoric acid or phosphorus was observed.

Catalyst J-O

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. A slurry containing 12.09 g of NH₄-ZSM-5 zeolite and 50 ml of deionized water was prepared in a 400 ml beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a magnetic stir bar. The temperature of the suspension was maintained around 90° C. 1.08 g phosphoric acid (85 wt % in aqueous) was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The phosphoric-acid modified zeolite was dried at 90° C. to 120° C. for at least four hours and at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined zeolite was then crushed and sized using 20 and 40 mesh screens. A series of Catalysts J-N (see Table 2) were prepared by varying the amount of phosphoric acid with respect to the amount of starting NH₄-ZSM-5 powder. A non-phosphorus ZSM-5 (Catalyst O) was also prepared by calcining (using the same temperature profile described above) the NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. BET surface area and total pore volume (measured by N₂ adsorption) for catalysts J-O are shown in Table 2 and FIGS. 1 and 2. The decrease in BET surface area (SA) and total pore volume (PV) for catalyst made using starting NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio 280 is not as prominent compared to that for catalysts A-J prepared by using starting NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio 30.

TABLE 2 Water, Zeolite H₃PO₄ P, g/g PV, Catalyst ml Powder, g Content, g^(a) zeolite^(a) SA, m2/g ml/g J 50 12.09 1.08 0.024 330.7 0.208 K 50 24.09 3.95 0.044 299.4 0.182 L 100 48.38 15.8 0.088 183.2 0.138 M 100 48.39 23.7 0.123 156.2 0.113 N 50 12.09 7.75 0.172 163.7 0.120 O — — 0 0 375.0 0.244 ^(a)Total amount of phosphoric acid (85% in aqueous) or P used in the preparation. Catalyst P-S

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. A slurry containing 51.66 g of NH₄-ZSM-5 zeolite and 200 ml of deionized water was prepared in a 400 ml beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a magnetic stir bar. The temperature of the suspension was maintained around 90° C. 9.07 g ammonium hydrogen phosphate, (NH₄)₂HPO₄, was dissolved in 50 ml water and the salt solution was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The ammonium hydrogen phosphate modified zeolite was dried at 90° C. to 120° C. for at least four hours and at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined zeolite was then crushed and sized using 20 and 40 mesh screens. A series of Catalysts P-S (see Table 3) were prepared by varying the amount of ammonium hydrogen phosphate with respect to the amount of starting NH₄-ZSM-5 powder. BET surface area (SA) and total pore volume (PV) (measured by N₂ adsorption) for Catalysts P-S are shown in Table 3.

TABLE 3 Water, Zeolite (NH4)2HPO₄, P, g/g SA, PV, Catalyst# ml Powder, g g^(a) zeolite^(a) m2/g ml/g P 200 30.09 2.49 0.018 317.2 0.208 Q 200 51.66 9.07 0.039 278.3 0.179 R 200 51.66 12.85 0.055 241.0 0.155 S 200 48.38 18.14 0.082 216.2 0.131 ^(a)Total amount of ammonium hydrogen phosphate or P used in the preparation

There was little or no difference in surface area and pore volume between the catalyst series J-N made by using phosphoric acid and catalyst series P-S made by using ammonium hydrogen phosphate at a given amount of phosphorus. Thus the use of phosphoric acid or ammonium hydrogen phosphate as a phosphorus-containing compound for preparing p-xylene selective catalysts may not make a significant difference.

Catalyst T-W

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. A slurry containing 400.0 g of NH₄-ZSM-5 zeolite and 800 ml of deionized water was prepared in a 2 L beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a mechanical stirrer. The temperature of the suspension was maintained above 90° C. 182.5 g phosphoric acid (85 wt % in aqueous) was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The phosphoric-acid modified zeolite was divided into four samples and each sample was dried or calcined at different maximum temperatures: Catalyst T (dried at 60° C.), Catalyst U (dried at 250° C.), Catalyst V (calcined at 350° C.) and Catalyst W (calcined at 510° C.).

Solid State ²⁷Al MAS-NMR

Solid state Magic Angle Spinning (MAS) NMR spectra were recorded on the ZSM-5 zeolites with 400 MHz spectrometer (²⁷Al at 104.5 MHz) at room temperature. Samples were packed in silicon nitride rotors (Si₃N₄) and spun at 13 to KHz sample spinning (about 800000 rpm). A 10 degree tip and recycle delay of 0.5 s were used to avoid saturation. About 4000 to 10000 scans were accumulated to signal average and to improve signal/noise ratio. Proton decoupling was not employed. All spectra were referenced to aluminum chloride hexahydrate (run separately in a tube) at 0.0 ppm on the chemical shift scale. This leads to an internal reference of 104.85 ppm on the aluminum nitride (small impurity in the silicon nitride rotors) peak.

²⁷Al MAS-NMR spectra were recorded on the starting NH₄-ZSM-5 zeolite having SiO₂/Al₂O₃ mole ratio 280 and the phosphorus modified zeolites. The starting NH₄-ZSM-5 zeolite sample showed a strong ²⁷Al MAS-NMR peak at around 55 ppm attributing to framework tetrahedral (4 coordinated) aluminum (spectrum a, FIG. 3). The sharpness of the resonance and the symmetry indicate the zeolite is relatively crystalline with very few lattice defects. The framework Al is responsible for zeolite acidity and the starting zeolite sample showed strong acidity. The P-modified sample shows a weak peak at about 55-50 ppm region assigned to structural tetrahedral aluminum (spectrum b, FIG. 3). The tetrahedral aluminum peak is severely distorted, indicating presence of nested silanols caused by holes in the structure upon removal of some of the framework aluminum. The adjacent peak (30-40 ppm) peak is due to severely distorted but still in the framework aluminum atoms probably either in the 3 or 5 coordination with oxygens. The tallest peak in spectrum a at −14 ppm is from octahedrally coordinated aluminum atoms that are formed when tetrahedrally coordinated framework aluminum is removed from the zeolite framework by the phosphate modification process as mentioned above.

³¹P MAS NMR

MAS NMR spectra were recorded on the P/ZSM-5 zeolite with 400 MHz spectrometer (³¹P at 161.7 MHz) at room temperature. Samples were packed in silicon nitride rotors (Si₃N₄) and spun at 13 to KHz sample spinning (about 800000 rpm). A 30 degree tip and a recycle delay of 15 s were used to avoid saturation. About 4000 to 10000 scans were accumulated to signal average and improve signal/noise ratio. Proton decoupling was not employed. All spectra were doubly referenced to tetramethyl diphosphine disulphide at 37.8 ppm and 85% phosphoric acid (run separately in a tube) at 0.0 ppm on the chemical shift scale.

³¹P MAS-NMR spectra were recorded on the P-treated ZSM-5 (SiO₂/Al₂O₃ mole ratio 280) after drying or calcining at different temperatures. A strong peak at around 0 ppm and a weak peak at around −11 ppm were observed for P/ZSM-5 after drying at 60° C. (catalyst T, FIG. 4, spectrum a). The peak at about 0 ppm may be assigned to free phosphate occluded in zeolite pores/channels. As the drying or calcining temperature was increased the peak at about 0 ppm decreased with the appearance of new peaks of from about −20 ppm to about −50 ppm (catalyst U-W, FIG. 4, spectra b-d). The weak peak observed at about −11 ppm remained almost unchanged with the change of drying/calcining temperature. The peaks at about −11, about −31 and about −44 ppm were assigned to phosphorus bound to various phosphorus species such as extra-framework Al, AlPO/SAPO and polyphosphate. Apparently, the state of phosphorus in the zeolite changed during drying/calcinations.

X-Ray Diffraction Pattern (XRD)

The X-ray diffraction patterns (XRD) of NH₄-ZSM-5 and P-treated catalysts (U-W) were recorded on a Philips (X'Pert model) diffractometer over a range of 5-55° at a scan rate 2° per minute using CuKα1 radiation. The peak intensities of the ZSM-5 decreased after the P-treatment of NH₄-ZSM-5 zeolite. Apparently, the P-treatment caused some damage to the initial zeolite structure. The P-treated ZSM-5 catalyst started to show new peaks at d-spacing 8.02, 6.53 and 3.52 Å after catalyst dried at 250° C.; the intensities of the new peaks increased further when the catalyst was dried/calcined at 350° C. and 510° C. The X-ray diffraction peaks are set forth in Table 4 below.

TABLE 4 Powder XRD Intensity* d-spacing [Å] Intensity d-spacing [Å] Intensity 11.09 100 5.56 9 10.00 55 4.25 9 9.88 42 4.00 6 9.68 17 3.84 50 8.02 8 3.81 31 6.68 7 3.71 27 6.53 8 3.64 10 6.33 8 3.52 22 5.98 16 2.98 8 5.69 7 2.78 5 *Intensities shown are scaled in arbitrary units so that most intense peak is 100.

EXAMPLES 1-19

The catalysts A-I, J-O and P-S described above and in Tables 1-3, were used in toluene methylation reactions. The reactions were each carried out in a fixed bed, continuous flow type reactor. In each case, a catalyst was dried by slowly raising the catalyst bed temperature (about 5° C./min) to 200° C. under hydrogen (H₂) flow for at least one hour. A premixed methylation feed of toluene and methanol (molar ratio 2/1) was added to the reactor at 200° C. and the catalyst bed inlet temperature was increased to about 500° C. The liquid hourly space velocity (LHSV) (based on methylation feed) was maintained at about 31 hr⁻¹ and a cofeed of H₂ gas was fed and maintained to provide a H₂/(toluene+methanol) molar ratio of about 0.1. Water was added to the methylation feed and was vaporized prior to introduction to reactor. The H₂O/(toluene+methanol) molar ratio was about 0.65 and reactor pressure was about 20 psig. Liquid products were collected at about 3-4 hours of run time and were analyzed. The following results, as presented in Tables 5-7. FIG. 5 is a plot of para-xylene slectivity and selectivity for total xylenes for catalysts A-I. FIG. 6 is a plot of para-xylene selectivity and selectivity for total xylenes for catalysts J-O.

TABLE 5 Catalyst A B C D E F G H I Example Product Analysis, wt %¹ 1 2 3 4 5 6 7 8 9 Water 21.06 21.50 21.61 21.90 19.02 18.21 16.54 17.27 21.72 Methanol 0 0.10 0.15 0.75 4.05 4.64 5.37 6.48 0.08 Dimethylether 0 0 0 0 0 0 0 0 0 Benzene 1.39 1.18 0 0 0 0 0 0 0.43 Toluene 43.82 44.77 50.54 54.86 70.21 72.00 75.33 74.11 49.63 Ethylbenzene 0 0 0 0 0 0 0 0 0 p-Xylene (PX) 7.11 6.85 12.35 14.30 5.58 4.49 2.65 2.03 5.86 m-Xylene (MX) 15.44 14.88 8.94 4.20 0.47 0.26 0.11 0.11 12.48 o-Xylene (OX) 6.86 6.58 3.46 1.82 0.30 0.17 0 0 5.38 Ethyltoluenes 1.01 0.95 0.42 0.26 0.14 0.11 0 0 1.18 Trimethylbenzenes 2.94 2.84 2.33 1.75 0.22 0.12 0 0 2.81 C10+ 0.36 0.36 0.20 0.16 0 0 0 0 0.41 Total Aromatic Products, wt % 35.11 33.64 27.70 22.49 6.71 5.15 2.76 2.14 28.55 Total Xylenes, wt % 29.41 28.31 24.75 20.32 6.35 4.92 2.76 2.14 23.72 Total Xylenes Selectivity, wt % 83.77 84.16 89.35 90.35 94.63 95.53 100 100 83.08 p-Xylene Selectivity, wt % 24.17 24.20 49.90 70.37 87.87 91.26 96.01 94.86 24.70 ¹Liquid product stream analysis

TABLE 6 Catalyst J K L M N O Example Product Analysis, wt %¹ 10 11 12 13 14 15 Water 16.33 16.80 19.73 16.38 15.79 16.12 Methanol 0.54 0.50 2.39 1.72 2.13 0.45 Dimethylether 0 0 0 0 0 0 Benzene 0 0 0 0 0 0.39 Toluene 57.02 57.76 60.57 64.47 66.10 52.37 Ethylbenzene 0 0 0 0 0 0 p-Xylene (PX) 19.55 20.18 15.05 15.24 13.37 8.54 m-Xylene (MX) 3.12 2.04 0.76 0.84 0.96 13.70 o-Xylene (OX) 1.56 1.07 0.48 0.53 0.68 5.50 Ethyltoluenes 0.35 0.36 0.32 0.35 0.33 0.67 Trimethylbenzenes 1.39 1.17 0.45 0.47 0.55 2.05 C10+ 0.12 0.11 0.25 0 0.09 0.20 Total Aromatic Products, 26.09 24.93 17.31 17.43 15.98 31.05 wt % Total Xylenes, wt % 24.23 23.29 16.29 16.61 15.01 27.74 Total Xylenes Selectivity, 92.87 93.42 94.11 95.30 93.93 89.34 wt % p-Xylene Selectivity, wt % 80.69 86.65 92.39 91.75 89.07 30.79 ¹Liquid product stream analysis

TABLE 7 Catalyst P Q R S Example 16 17 18 19 Product Analysis, wt %¹ Water 17.65 16.46 16.22 16.58 Methanol 0.57 0.85 0.98 2.27 Dimethylether 0 0 0 0 Benzene 0 0 0 0 Toluene 56.17 60.21 61.74 66.50 Ethylbenzene 0 0 0 0 p-Xylene (PX) 19.87 18.17 18.34 13.34 m-Xylene (MX) 2.53 1.76 1.05 1.06 o-Xylene (OX) 1.47 0.98 0.58 0.25 Ethyltoluenes 0.35 0.36 0.41 0 Trimethylbenzenes 1.25 1.08 0.68 0 C10+ 0.13 0.12 0 0 Total Aromatic Products, wt % 25.60 22.47 21.06 14.65 Total Xylenes, wt % 23.87 20.91 19.97 14.65 Total Xylenes Selectivity, wt % 93.24 93.06 94.82 100 p-Xylene Selectivity, wt % 83.24 86.90 91.84 91.06 ¹Liquid product steam analysis

While the invention has been shown in only some of its forms, it should be apparent to those skilled in the art that it is not so limited, but is susceptible to various changes and modifications without departing from the scope of the invention. Accordingly, it is appropriate that the appended claims be construed broadly and in a manner consistent with the scope of the invention. 

1. A catalyst comprising a phosphorus-containing ZSM-5-type zeolite having a silica/alumina molar ratio of at least 200, the phosphorus-containing ZSM-5-type zeolite having a phosphorus content of at least 8% by weight of zeolite and having multiple phosphorus species exhibited by at least three ³¹P MAS NMR peaks with maxima at from about 0 to about −50 ppm.
 2. The catalyst of claim 1, wherein: the zeolite is a bound zeolite.
 3. The catalyst of claim 1, wherein: there are multiple phosphorus species exhibited by three ³¹P MAS NMR peaks with maxima at about 0 ppm, about −11 ppm, about −31 ppm or about −44 ppm.
 4. The catalyst of claim 1, wherein: there are multiple phosphorus species exhibited by ³¹P MAS NMR peaks with maxima at about 0 ppm, about −11 ppm, about −31 ppm and about −44 ppm.
 5. The catalyst of claim 1, wherein: the phosphorus-containing ZSM-5-type zeolite has a total pore volume of 0.2 ml/g or less.
 6. The catalyst of claim 1, wherein: the phosphorus-containing ZSM-5 zeolite has a BET surface area of from about 300 m²/g to about 10 m²/g.
 7. The catalyst of claim 1, wherein: the phosphorus-containing ZSM-5-type zeolite exhibits powder X-ray diffraction peaks as shown in Table
 4. 8. The catalyst of claim 1, wherein: the phosphorus-containing ZSM-5-type zeolite has a total pore volume of 0.18 ml/g or less.
 9. The catalyst of claim 1, wherein: the zeolite has a ratio of framework aluminum to extra-framework aluminum as measured by ²⁷Al MAS-NMR of 0.12 to 0.25.
 10. The catalyst of claim 1, wherein: the zeolite has silica/alumina molar ratio of at least
 280. 11. The catalyst of claim 1, wherein: the zeolite has a silica/alumina molar ratio of at least 200 to
 1000. 